Re: High freelime and liter weight

The most likely reason for this problem is that the lime saturation is higher than can possibly combined in the CSAF ...

Re: USE OF PC DUCT WITHOUT PH DUCT WITH BOTH FANS

Dear Mr Mothia, Without more information on the duct configuration and how it is possible to operate with only the P...

Re: NO Reduction in reburning conditions

The temperatures in an in-line calciner are too high for ammonia or uea injection. That must be in the preheater. It...

Re: NO Reduction in reburning conditions

You will also see reference to "staged combustion" in relation to NO reduction in cement kilns. This staged combusti...

Re: Residue of cement in open circuit mill

Air flow rate will affect residue as fines will be stripped off the charge in the mill before they have time to be gr...

Re: Residue of cement in open circuit mill

There could be a number of reasons: (i) changes in grindability of the clinker, or (ii) variation in the condition of...

Re: Kiln Ring Formation

No Naison, the SO3 content of clinker will not tell us the degree of SO3 concentration or potential build-up formati...

Re: Kiln Ring Formation

Are you still experiencing this ring formation Naison? At that position the root cause is most likely excessive SO3 ...

Re: Kiln Shell cooling system

I suggest you contact Phillips Rema kiln services, www.phillipsrema.co.uk .

Re: Kiln Material Bypass

Wasting hot meal from the bottom stage cyclone will work just as well as wasting hot gas wth its load of dust and ev...