coal residue effect

Dear friends, what is the effect of increasing coal petcock residue upto 17% in 80 micron in the kiln pyro-process...

re free lime

thanks alot mrTed,also my laboratory colleages tell me that when LSF is low the amount of C2S will be more or equa...

free lime

hello mr Ted if free lime is very low like 0.5 ,lead to reduce 28 days strength . if yes why?

re kiln torque derivation against motor power?

power= torque * angular velocity angular velocity = 2pi rotational velocity so torque = powe/ 2pi rpm

kiln voulme loading

% loading = 1.5 Wt/LA               =0.35 Wt/LA               = 1.67 Wt/LA which factor is correct , i fo...

re High MgO in limestone

Thanks a lot Mr.Ted

re High MgO in limestone

"you may have to grind your cement a bit finer to help counteract magnesia expansion" would you please explain ...

re K. F

thanks mr Ted , in addition to that you mentioned i read one paper tell that the volume of AL is more than Fe due ...

K. F

although IRON OXIDE is more flux than ALUMINUM OXIDE and also it gives low viscose L PH but always alumina is more...

re Positive Pressure after preheater fan outlet

  i will give you some suggestions 1/readjusting your dampers and control dust load intrering your filter 2/...