Re: rawmix homo silo efficiency

Hello Emad, I agree with Lalbatros. The FLS homogenising factor H is given by;- H = Ö ...

Re: Effect of reducing raw meal SO3 in clinker alkali

Hello Erj, There is no chemical reaction that can reduce alkalis in the kiln system. Chemical inputs must balan...

Re: low sulfur/alkalis ratio

Hello Emad, The possible negative effects of a low Sulphur/Alkali ratio are that;- 1. The excess of alkalis over s...

Re: Excess O2 & Boulder Formation

Hello Emad, From your information above it does not look like sulphur or alkalis are an issue. The MgO is a little ...

Re: Excess O2 & Boulder Formation

Hello Emad, Yes, high SR can cause dusty clinker due to a corresponding reduction in the amount of liquid phase pre...

Re: GRATE COOLER

Hello Afsal, What you are describing is a common problem in clinker coolers and is generally called a "Red River". ...

Re: Shale vs Limestone

Hello CVN, You have to be more specific, because 'high' insoluble residue means different things depending on the m...

Re: Alternative Free-Lime determination

Hello Norew, You can use glycerol (glycerin or glycerine) as an alternative to Ethelyene Glycol. However slightly l...

Re: density of raw meal

v.raginishah@flsmidth.com: what units have you specified the density also are you referring to Material Bulk...

Re: Waste Recycling

Hello Norew, If the the quantity of waste mortar disposed of at any one time is not too large (ie. less than 100kg)...