PRICE FOR PORTLAND CEMENT 42.5 ORIGIN UKRAINE
PRICE 105 USD/MT ON CIF CONDITION
MIN ORDER; 150 000 MT
Specifications:
Grey Ordinary Portland cement Construction Grade 42,5 N/R
United States ASTM C-150, British BS 12/1996, or European EN-197 1/2000 or GOST
Portland cement 42.5 R
CHEMISCHE COMPOSITIO:
Loss in ignition 1.8
Insoluble residue 0.8
Sulphur trioxide 2.7
Magnesia, MGO 1.7
Chloride 0.7
NA2O equivalent 0.24
HYPOTHETICAL COMPOUND COMPOSITION:
Try calcium silicate, c3s 54.4
Di calcium silicate, c2s 18.2
Try calcium acuminate, c3a 6.8
Tetra calcium alumni ferrite, c4af 11.6
Normal consistency 27.5
Fitness index(cm^2/gm) 3040
Initial set(hours: mints) 3:25
Hard set(hours: mints) 4:52
COMPRESSIVE STRENGTH ISO/en 196 mortar Bs 4550 mortar
3 days (n/mm^2) 26.5 34.2
7 days (n/mm^2) 37.3 42.5
28 days 52.8 54.6
w/c ratio 0.5 0.4
Laboratory cured at 22 (plus -minus 2c)
Portland Cement 42.5 N
CHEMISCHE COMPOSITIO:
SILICON DIOCIDE 20, 88
ALUMINIUM OXIDE (A1203) 4,29
FERRIC OXIDE (FE203) 4,13
CALCIUM OXIDE (CAO) 65,08
MAGNESIUM OXIDE (MGO) 0,78
SULPHUR TRIOXIDE (SO3) 2,88
LOSS OF IGNITION (LOI) 0,65
TRICALCIUM SILICATE (C3S) 61,06
DICALCIUM SILICATE (C2S) 17,00
TRICALCIUM ALLUMINATE (C3A) 4,70
TRICALCIUM ALUMINO FERRICE (C4AF) 13,50
PHSICAL AND MECAHICAL PROPERTIES
BLAIN CM/GR 3.150
AUTOCLAVE EXPATION 0.02
ITIAL SETTING TIME (VICAT) 205 MINUTES
FINAL SETTING TIME (VCAT) 265 MINUTES
COMPRESSIVE STRENGTH
@ 03DAY 205 KG/CM2
@ 07DAYS 305 KG/CM2
@ 28 DAYS 527KG/CM2
SPECIFICATIONS AND CHEMICAL COMPOSITION OF GREY ORDINARY PORTLAND CEMENT
CHEMICAL COMPOSITION
CHEMICAL ANALYSIS | UNIT | CONTROL RANGE | TYPICAL |
? | ? | ? | ? |
SILICON DIOXIDE (SiO2) | % | 20.0 - 23 | 21 |
ALUMINIUM AXIDE (Al2O3) | % | 4.5 ? 6.0 | 5.30 |
FERRIC OXIDE (Fe2O3) | % | 3.1 ? 6.0 | 3.30 |
CALCIUM OXIDE (Cao) | % | 64 - 68 | 65.60 |
MAGNESIUM OXIDE (Mgo) | % | 1.0 ? 5.0 | 1.10 |
SULPHUR TRIOXIDE (SO3) | % | 1.9 ? 3.0 | 2.70 |
LOS OF IGNITIION (Loi) | % | 1.0 ? 3.0 | 0.90 |
TRICALCIUM SILICATE (C3S) | % | 50.0 ? 60.0 | 60.00 |
DECALCIUM SILICATE (C2S) | % | 15.0 ? 25.0 | 15.00 |
TRICALCIUM ALUMINATE ( C3A) | % | 7.5 ? 9.5 | 8.05 |
TRIC. ALUMINO FERRICE (C4Af) | % | 8.5 ? 10.5 | 9.76 |
?
PHYSICAL AND MECHANICAL PROPERTIES
PHYSICAL ANALYSIS | UNIT | CONTROL RANGE | TYPICAL |
? | ? | ? | ? |
BLAINE FINENESS | m2/Kg | 300 -380 | 360 |
TIME OF SETTING (VICAT) INITIAL SET FINAL SET | ? MIN. MIN. | ? 70 -150 130 -300 | ? 135 210 |
COMPRENSIVE STRENGTH 3 DAYS 28 DAYS | ? Mpa Mpa | ? 22 -31 46 - 56 | ? 27 54 |
PRICE FOR PORTLAND CEMENT 42.5 ORIGIN GERMANY
PRICE 106 USD/MT ON CIF CONDITION
MIN ORDER; 50 000 MT
SPECIFICATION OF ORDINARY PORTLAND CEMENT
AS PER BS EN 197-1:2000 UNDER NOTATION
CEM I 42,5N
items | CEM I 42,5N |
Chemical Properties: | ? |
Loss Of Ignition (L.O.I) | Maximum 3.0% |
Magnesium Oxide (MGO) | Maximum 4% |
Sulphur Trioxide (SO3) | Maximum 3.0% |
SILICON DIOXIDE(SIO2) | Minimum 20 % |
ALUMINIUM OXIDE (AL2O3) | Maximum 6% |
FERRIC OXIDE (FE2O3): | Maximum 6% |
TRiCALCIUM ALUMINATES (C3Al)?? | Maximum 8% |
tricalcium silicate (C3S)? | Maximum 50% |
Alkalies K2O& Na2O | Maximum 0.6% |
Insoluble residues | Maximum 0.75% |
?
Physical Properties: | |
Soundness Autoclave expansion | Maximum 0.8% |
Surface area cm2/gm | Not less than 2800 |
initial Setting Time (Vicat)? | Minimum 45 min |
Final Set Time (Vicat) | Maximum 375 min |
Compression Resistance N/mm2 | Cubes 5 x 5 x 5 cm Minimum 42.5 ( 28 days) |
Hydration KJ/Kg after 7 days | Maximum 290 KJ/Kgm |
PRICE FOR PORTLAND CEMENT 42.5 ORIGIN US-UKRAINE-BRAZIL
PRICES CEMENT 42.5 R-N
1 year contract | price USD$ per MT CIF |
SPOT = 25000 MT | 100.00 |
12.500 x 12 months = 150.000 MT | 81.50 |
25.000 x 12 months = 300.000 MT | 79.50 |
50.000 x 12 months = 600.000 MT | 77.50 |
100.000 x 12 months = 1.2 Million | 76.50 |
250.000 x 12 months = 3 Million | 75.00 |
500.000 x 12 months = 6 Million | 74.00 |
Further than 6 Million | 73.50 |
FOR MORE THAN 10,000,000MT OUR PRICE IS $60,00/MT
(CEMENT PRICES ARE SUBJECT TO USD$ CURRENCY FLUCTUATION SO MIGHT CHANGE ANY TIME)
FOR CEMENT OPC 52.5 R-N PLEASE ADD 7 US$ ON EVERY PRICE
FOR CEMENT OPC 32.5 R-N PLEASE 1 US$ LESS ON EVERY PRICE
SABS CERTIFICATE ADDING USD$ 10.00 PER MT
GOST CERTIFICATE ADDING USD$ 40.00 PER MT
ORIGIN
US– UKRAINE – BRAZIL
NO CHINA PRODUCT !!!
PACKING: 50 KG BAGS OR BULK – JUMBO BAGS – BUYERS OPTION
DELIVERY: WITHIN THIRTY (30) TO FOURTY FIVE (45) DAYS AFTER RECEIPT OF OPERATIVE PAYMENT INSTRUMENTS
PAYMENTS
SELLER ACCEPTS: BANK GUARANTEE – STAND BY LETTER OF CREDIT – SWIFT MT 103/23 – TT
AND / OR
REVOLVING DOCUMENTARY LC (RDLC) – FULLY FUNDED REVOLVING DOCUMENTARY LC (FFRDLC) adding 2 USD$/MT!!!
AND / OR
NON-TRANSFERABLE DOCUMENTARY LC (DLC) adding 5 USD$/MT (as long as the Seller is First Beneficiary)
PRODUCT
GREY PORTLAND CEMENT 42.5 N/R
Conform to British standard specifications bs12/1996 or ASTM C-150
Certified accordingly to EN 196
SPECIFICATIONS
CHEMICAL ANALYSIS |
|
SIO2 SILICON DIOXIDE | 20% MIN |
A120 ALUMINIUM OXIDE | 6.0% MAX |
FE 203 FERRIC OXIDE | 5.0% MAX |
CAO CALCIUM OXIDE | 62.0% MIN |
MGO MAGNESIUM OXIDE | 3.0% MAX |
SO3 SULPHUR TRIOXIDE | 3.0% MAX |
LOI LOSS OF IGNITION INSOLUBLE RESIDUE TOTAL ALKALIES AS NA2O | 3.0% MAX 0.50% MAX 0.6 % MAX |
C3A TRICALCIUM ALUMINATES | 8.0% MAX |
C3S TRICALCIUM SILICATE | 55.00% MIN |
C2S DICALCIUM SILICATE | 25.0% MAX |
C4AF TRICALCIUM ALUMINOUS FERRIC | 9.76% MAX |
PHYSICAL TESTS |
|
FINENESS | 400 MAX |
BLAINE | 3.250 CM2/G |
AUTOCLAVE EXPANSION | 0.02 MM |
COMPRESSIVE STRENGTH |
|
1 DAY (PSI) | 2000 MIN |
3 DAYS (PSI) | 3100 MIN |
7 DAYS (PSI) | 4500 MIN |
28 DAYS (PSI) | 5800 MIN |
TIME OF SETTING |
|
INITIAL SETTING TIME (VICAT TEST) | 80 MIN |
FINAL SETTING TIME (VICAT TEST) | 250 MAX |