Impact of ALKALY, SULPHURE and CHLORINE in Kiln operation and clinker quality ?

Dear All,

regarding circulating element in kiln section like Cl,SO3 and alkaly. 

some question I want to discuss with community ,hope this is the right forum to resolve my query.

 

1.) why and how we can set the control limit of alkaly/sulphure ratio in kiln system between(0.8 to 1.2) ? ( any analytical derivation)

2.) what happen in kiln operation as well as clinker quality ( any reaction ) when alkaly goes very high in circuit ?

3.) What happen in kiln operation as well as clinker quality (any reaction ) when SO3 goes very high in  kiln circuit?

4.) What happen in kiln operation as well as clinker quality (any reaction ) when Cl goes very high in  kiln circuit?

best regards

raju verma

 

 

 

 

 

 

Reply

Know the answer to this question? Join the community and register for a free guest account to post a reply.

re Impact of ALKALY, SULPHURE and CHLORINE in Kiln operation and clinker quality ?

Hello Raju,

To answer your questions;-

1. The alkali/sulphur ratio is used in two ways in kiln operation. The first is to measure if there is a molar balance between the total inputs of alkalis and sulphur contributed by all of the raw materials, fuels and AFR streams entering the kiln...  the second is to measure the instantaneous molar alkali/sulphur balance in the kiln/preheater system (based on hot meal)

Both use the same equation;-

            { K2O/94) + (Na2O/62) - (Cl/71) }
A/S =   --------------------------------------------
                              (SO3/80)

However, if there is little or no chloride in the raw material and fuel inputs to the kiln, the chloride component is often ignored when calculating the A/S ratio of the total inputs.

For hot meal though, chloride is always subtracted from the alkali molar total because alkali chlorides are far more volatile than alkali sulphates and recirculate within the kiln. (Over 98% of alkali chlorides (particularly KCl) are re-evaporated in the high temperature of the burning zone and return to thekiln inlet with the kiln gases where they condense on the incoming hot meal and continue to recycle.)    Any K2O or Na2O tied up with the chlorides are therefore not considered in the A/S ratio calculation for hot meal.

The purpose of the hot meal A/S ratio is to predict the likelihood of alkali or sulphur related buildups in the kiln inlet. In particular, sudden decreases in this ratio can indicate lack of oxygen in the back end of the kiln and impending sulphur buildups.  A high value indicates an excess of alkalis. The portion of the alkalis which do not combine with SO3 to form sulphates will also recirculate in the kiln, increasing the potential for rings and preheater buildups.

When applied to the kiln material inputs, the alkali/sulphur ratio is used to manage raw material, fuel and AFR inputs. New raw materials, fuels and AFRs should be chosen taking their effect on the overall akali/sulphur ratio into consideration. Similarly, selective mining can "fine tune" the chemistry of existing raw materials to optimise the raw mix alkali/sulphur ratio, if it is  not within the range 0.8 --> 1.2

2. If alkalis are very high and are not balanced by sulphur, it will be very difficult for them to exit the kiln. They will therefore continue to recirculate within the kiln/preheater system and increase the probabliity of kiln rings and preheater buildups. Clinker quality may suffer because free alkalis can enter into solid solution within the clinker minerals affecting their reactivity.

3. If sulphur is very high and is not balanced by alkalis, it will also continue to recirculate within the kiln/preheater system and increase the probabliity of kiln rings and preheater buildups. Excess sulphur in the hot meal can also form sulphospurrite (2(CaO).SiO2.CaS04) in the middle cyclones, which forms exceedingly hard and dense buildups which can take a long time to remove.   Clinker quality would also suffer because sulphur which is not combined with alkalis forms a solid solution with the silicate minerals, particularly C2S (up to 2%). Sulphur incorporated in this way stabilises C2S and inhibits its reaction with CaO to form C3S. As a result, C2S content is increased and C3S content is decreased in the clinker, causing a reduction in cement strengths.

4. If chloride is very high, it will first combine with all of the alkalis present forming alkali chlorides which will recirculate in the kiln and increase the probability of buildups in the preheater. Any remaining chloride will then combine with CaO to form CaCl2 which has a very low melting point (770-780oC). This will make the hot meal extremely "sticky" at this temperature and increase the chance of buildups higher up the preheater. Chlorides also form eutectic mixtures with sulphates of potassium, sodium, calcium and magnesium. These eutectic mixtures have melting points much lower than that of the pure compounds, further increasing the likelyhood of rings and buildups.  Above 0.015%, in the raw meal, chloride recirculation is so bad that blockages in the preheater are eventually inevitable. If the chloride does manage to escape the kiln(ie during kiln trips, stoppages etc), too much chloride in the clinker can accelerate the corrosion of reinforcing steel in the concrete.

Hope this helps...

Regards,
Ted.

Reply

re Impact of ALKALY, SULPHURE and CHLORINE in Kiln operation and clinker quality ?

Dear  Ted,

Could you please , advice about   detaled calculation of Molar alkali/Sulfo ratio, As I now we have to calculate this parameter of input raw meal with  total sulfur of raw meal and coal ,values from Hot meal are .necessary. . can we calculate  this parameter for clinker as well??

Thank you in advance

BR

Reply

re Impact of ALKALY, SULPHURE and CHLORINE in Kiln operation and clinker quality ?

Hello ,

If my alkalis and sulphur kept constant and sudden increase of chloride from 0.22 to 0.28 what is

its effect on kiln operation ? and clinker lime percentage ?

Which parameter deviates in kiln operation.

 

Thanku

Reply