re Yet Another Raw Mix Design program
When calling Solver from VBA, there must be a reference to solver.xlam (xla if version 2003 or older). I guess tha...
re Conditioning tower problems
If it is 15 years old, it may not be with air for atomizing the water, In that case the water pressure can be too ...
re Residence time inside Kiln
I doubt it matters much for the residence time. Unless you increase production the gas volume through the kiln wil...
re Cooler ESP high dust emission
Try water injection to reduce the dust's resistivity. It should have a dramatic effect.
re snow man
Ted's explanation is plausible. Another factor could be that after removing rhino build ups your flame has become ...
re Bypass Chloride
I have heard some report problems at 12-13% Cl, however we have never had problems. I presume temperature and part...
re limestone and viscosity
Sodium tripolyphosphate can work immediately (minutes), but is more expensive than soda. My experience is that sod...
re High free lime in clinker
Could be a sulphur cycle inside the rotary kiln. If the kiln is dusty the SO2 may not reach the calciner. CaSO4 de...
Re: Cooling Schedule
We usually cool for 24 hours, and the ID-fan(s) are running to remove the heat. After 24 hours you should be able to...
Re: C3A by XRD
If your clinker SO3 is in excess of alkalies some Al can be incorporated into the silicates. Orthorhombic C3A is "dop...