Burning Question 87
What is the optimal forced air flow on the kiln shell? How does this impact on the refractory life? What is the inter...
Re: Burning
I would say the optimum forced air flow on the kiln shell is zero. The higher the air flow then the higher is the los...
Burning Question 88
We have a hot spot at 22m on our kiln, would it be possible to use a jet of water to cool the shell in this area?
Re: Burning
People sometimes do that. However, it causes a significant blemish on the shell and when the water is switched on a s...
Burning Question 89
I want to make a complete evaluation of the cement lines in my plant by doing a mass and heat balance, how do recomme...
Re: Burning
Your idea is a good one to understand the process and construct the mass and heat balances. First you need to measure...
Burning Question 90
We are running for the last one year with a rapid build up at mix chamber, kiln housing and stage 4 riser and counter...
Re: Burning
Possibly the feed flap from stage 3 being stuck open is causing short-circuiting of gases from the calciner and the d...
Burning Question 91
I am a Chemical Engineer working in a company in the cement area in South America and the question is: What sort of f...
Re: Burning
In my experience acid grade fluorspar spar is used as a mineraliser, however there is no reason why other grades shou...