Belite: It may not be dust. If the burner protrudes into the kiln, the reason may very well be that sticky ma...
Dastgir: Alkali sulphate, perhaps, will not have to do much here, since it should be evaporating back towards...
Dastgir: How much gypsum consumption is generally encountered for nominal setting times, if the plant is utili...
Dastgir: It means that free lime be on higher side, if we use Pet coke? Hello Gulam, Only if there is no...
Dastgir: Little confusion. Due to non conversion of C2S to C3S, because of high SO3, latter strength should h...
faslan: For example, how I can find the Flourine content in a rock. Because X-Ray can not read F. Do you know ...
Hello Firat, Based on what you have told me so far, I suspect that your problem is to do with an excessive clinker ...
There is another factor which can cause low strengths in cement made from high SO3 clinker. In excess of that requi...
faslan: What I've read from the Holderbank's notes unstable coating, ring & ball formations are affected by t...
faslan: First question can you describe the quality effect of fineness deeply? Raw meal fineness directly ...
;