Ted Krapkat
Registered User
Gladstone, Queensland, Australia.
Plant Chemist, Cement Australia.
Hello Vinay, One possible reason is that your raw meal burnability is poor. Poor burnability will result in dense, ...
armankhan: thanks to all my friends for reply..... friends plz tell me in which case we to become compell...
Hello Armankhan, Like sand, the role of sandstone is usually as a silica corrective. If used in the raw mix, sands...
Hi, Ammonia forms more readily under reducing conditions. It will then react preferentially with the hot meal chlo...
cemcem: Can anybody share experiences on HCl emissions and what the influences of the process on the HCl level...
David: Our kiln is 3000 tpd, with off line PC and 5 stages PH, our fuel is natural gas, H2S content in the gas...
fluence sysbacip: We are trying our best to get rid of this soft brown core but still no use we have oxygen a...
armankhan: please sir explain the kiln feed dust losses. as in our system we take hot gases frm kiln for rawm...
Hello CCC, I presume you have analysed the limestone fines? Do you add clinker/kiln dust of any sort to your cemen...
Hello Prisoner, A longer than optimum burning zone will promote the formation of large alite (C3S)crystals due to t...
;