Hello Norew, For a given C3A and gypsum content, finer grinding will accelerate the C3A hydration reaction. If the ...
Hello Dilip, Orthorhombic C3A (sometimes called alkali-aluminate) is formed when alkalis particularly Na) become ar...
Hello Dilip, But the finer the cement, the faster the C3A hydration reactions will occur and this will tend to re...
Hello Dilip, If the fineness of a cement is increased significantly, then the finer C3A may require extra SO3 to re...
Hello Armankhan, Yes, as Vikpro pointed out, you made an error in typing your clinker analysis results. I assumed t...
Hello Raj, I have emailed you a detailed reply just now. Let me know if you need any further clarification on anyth...
Hello Norew, During hydration, clinker silicate minerals in the cement react with water to form calcium silicat...
Hello Pankaj, As clinker nodules form they are initially quite porous structures. However as more liquid phase infi...
Hello Norew, I have received your questions and will respond to them as time permits. Regards, Ted. ...
Hello Pankajbits, All other factors being equal, low free lime clinker (hard burned) is generally harder to grind t...
;