Ted Krapkat
Registered User
Gladstone, Queensland, Australia.
Plant Chemist, Cement Australia.
norew: how Ca(OH)2 + HCl increases free lime? Norew, I'm not sure what you mean. Ca(OH)2 + HCl doesn't ...
Calahan/Lalbatros, Liquid phase should theoretically have a negative correlation with 28d strength because of its i...
Hello Sheikh, As the boulder/ring grows, you will see an increase in the pressure drop across the kiln, due to the ...
Hello Norew, Could you please be more specific. Regards, Ted.
Hi Nael, I don't think that it is the low O2 at the kiln inlet that makes the flame longer but rather, the other wa...
Hello Nael, Yes, there is a relationship between low kiln inlet O2 and the appearance of boulders. Low O2 in the ...
Hello Raza, The 'Free silica' in question is quartz or other hard high-silica mineral. Since quartz is very hard it...
Bandari.K: Please give me some suggestion regarding how to control the Cooler Static Grate Snowman & frequent...
Hello Vinay, The high quantity and viscosity of liquid phase is probably causing your balling problems. You need to...
lalbatros: In Cement Chemistry by Taylor (table 7.5), the heat of full hydration of c3s and c2s are given as...
;